We are going to talk about 5 key material parameters of tungsten carbide. Academically, cemented carbide is an alloy material with extremely high hardness and good wear resistance, which is made of tungsten carbide powder (hardened phase) of high hardness refractory metal as the main component and metals such as cobalt and nickel (bonding phase) as the binder, through ball milling, pressing and sintering. We can simply understand it as a metal material with high hardness and good wear resistance.

According to the relevant parameters of physics, the mechanical properties of cemented carbide are mainly shown in the following material parameters:

1. Bending strength material parameter

The bending strength of cemented carbide is lower than that of high-speed steel. Even YG8 cemented carbide with high bending strength has only about half of that of high-speed steel. The higher the cobalt content in cemented carbide, the higher its strength. With the same cobalt content, the bending strength of WC tic Co alloy decreases with the increase of TiC content. In addition to the types of carbides, the size of WC grains also affects the strength of cemented carbide. The bending strength of coarse-grained cemented carbide is higher than that of medium grain cemented carbide.

what are the 5 important material parameters of tungsten carbide 2

2. Compressive strength material parameter

The compressive strength of cemented carbide is very high, which can be 30%-50% higher than that of high-speed steel, about 3500-5600mpa, and the hot isostatic pressing product can reach 6000mpa. The compressive strength of cemented carbide is related to cobalt content, and the compressive strength is the largest when the cobalt content is 5%. The compressive strength of fine grain cemented carbide is greater than that of coarse grain cemented carbide, and the compressive strength of YT cemented carbide is lower than that of YG cemented carbide, which decreases with the increase of TiC content. Adding a small amount of TAC, NBC, VC, etc. can refine WC grains and improve the compressive strength.

Because the compressive strength of cemented carbide is much higher than the bending strength, when designing the tool structure and selecting cemented carbide blades, we should try to make the tool head in the state of compressive stress and less bending moment.

5 thông số vật liệu quan trọng của cacbua vonfram 3 là gì

3. Tensile strength material parameter

The tensile strength of cemented carbide is 750-1500mpa, about 1/4 of the compressive strength. Because there are many factors that affect the plasticity of cemented carbide materials, the tensile strength of a cemented carbide is usually within a certain range.

4. Impact toughness material parameter

The impact toughness of cemented carbide is lower than that of high-speed steel. The impact toughness of YG8 alloy with better performance is 30-40kj/m2, while that of W18Cr4V high-speed steel is 180-320kj / m2.

The impact toughness of cemented carbide containing tic decreases. When the tic content increases from 6% to 10%, the impact toughness decreases significantly. Temperature has a certain influence on the impact toughness of WC Co cemented carbide. At higher temperature, the impact toughness is improved.

Because the impact toughness of cemented carbide is lower than that of high-speed steel, it is not suitable to be used in the case of strong impact and vibration, otherwise it may cause cutting edge damage. The impact toughness of cemented carbide fluctuates greatly, and its absolute value is related to the test method. Therefore, when comparing the impact toughness of cemented carbide, the same instrument should be used to compare samples of the same size and shape.

5. Fatigue strength material parameter

Because the tool usually works under dynamic conditions, its fatigue strength is very important. The higher the cobalt content in cemented carbide, the higher the fatigue strength. The fatigue strength of cemented carbide is closely related to the surface quality of the sample. The better the surface finish, the higher the fatigue strength.

In terms of industry development, as China is in a critical period of manufacturing transformation and upgrading, high-end CNC tools and precision parts and molds, mainly made of cemented carbide, have long relied on imports as key industrial parts to improve manufacturing level and labor efficiency. These realistic conditions have become an obstacle to the transformation and upgrading of China’s manufacturing industry.5 thông số vật liệu quan trọng của cacbua vonfram 4 là gì

Therefore, at present, the main development direction of domestic cemented carbide products is to break through the technical barriers of high-end cemented carbide and realize the localization of high-end cemented carbide and its tools. Sidi Technology Co., Ltd. takes this as its own responsibility and vigorously supports the development of the domestic cemented carbide market.

Meetyou cemented carbide Co., Ltd. has provided global “customized” professional products and technical services for oil, natural gas drilling and production, chemical smelting, engineering machinery and other industries for 15 consecutive years. The company currently has 105 authorized patents, 34 invention patents, including 7 international patents, and its independently developed technology “cemented carbide composite forming technology”, Among them, the technical level of “cemented carbide high strength alloy additive manufacturing technology” is in the forefront of the world.